Manufactured from cross linked semi-conductive polyolefin.
Shrink temperature: start at 90℃, and fully recovered at 130℃.
Color: black.
Selection Table
| Spec. | As Supplied/mm | After Recovered/mm | Standard Cut Length/mm | Standard Continuous Length (m/roll) | ||
| Inner Diameter Min | Wall Thickness (±0.3) | Inner Diameter Max | Wall Thickness (±0.3) | |||
| WRSBG-45/17 | 45 | 0.9 | 17 | 2.3 | 400-1200 | 25 |
| WRSBG-50/20 | 50 | 0.9 | 20 | 2.3 | 400-1200 | 25 |
| WRSBG-55/23 | 55 | 0.9 | 23 | 2.3 | 400-1200 | 25 |
| WRSBG-60/24 | 60 | 0.9 | 24 | 2.3 | 400-1200 | 25 |
| WRSBG-65/25 | 65 | 0.8 | 25 | 2.3 | 400-1200 | 25 |
| WRSBG-75/29 | 75 | 1.0 | 29 | 2.7 | 400-1200 | 25 |
| WRSBG-90/30 | 90 | 0.8 | 30 | 2.7 | 400-1200 | 25 |
| WRSBG-100/36 | 100 | 0.9 | 36 | 2.7 | 400-1200 | 15 |
| WRSBG-120/37 | 120 | 0.8 | 37 | 2.7 | 400-1200 | 15 |
| WRSBG-150/55 | 150 | 0.8 | 55 | 3.4 | 400-1200 | 15 |
Technical Data
| Property | Test Method | Standard Value |
| Tensile Strength | ASTM-D-638 | ≥ 10MPa |
| Elongation at Break | ASTM-D-638 | ≥ 350% |
| Tensile Strength Variation After Heat Aging （130℃x168h） | ASTM-D-5510 | ≤± 20% |
| Elongation at Break Variation After Heat Aging （130℃x168h） | ASTM-D-5510 | ≤± 20% |
| Volume Resistivity | IEC 60093 | ≥1x103Ω.cm |
| Hardness（Shore A） | ISO 868 | ≥80 |
| Heat Shock | 160℃，4h | No Crack |
| Brittle Temperature | ISO 974 | -40℃ |
| Longitudinal Shrinkage | ASTM-D-2671 | ≤10% |
| Eccentricity | ASTM-D-2671 | ≤30% |